"[H]igher water content causes mixture too thin to accommodate bubbles... causing bubbles separating from the mixture..."
Foam concrete, also known as lightweight cellular concrete (LCC) and low density cellular concrete (LDCC), and by other names, is defined as a cement-based slurry, with a minimum of 20% foam entrained into the plastic mortar. As mostly no coarse aggregate is used for production of foam concrete the correct term would be called mortar instead of concrete; it may be called "foamed cement" as well. T
"Typically, the samples from the lowest part of the column were 16 to 32 kg/m3 (1 to 2 lb/ft3) denser than the samples from the top of the column. In extreme cases, variations as high as 320 kg/m3 (20 lb/ft3) were noted. Denser samples are stronger. In these low-density concretes, a 16- to 32-kg/m3 (1- to 2-lb/ft3) density difference can increase the unconfined compressive strength by 100 kPa (14.5 psi) or more."
"For fibreglass concrete, an alkali-resistant (AR) fibre should be used."
"[F]oamed concrete has the potential to become a mainstream material that uses waste material successfully as a replacement for cement or fine aggregate..."
"Various types of fibres allow the reduction of... autogenous shrinkage [by] a factor of 1.2–1.8 and drying shrinkage by a factor of 1.3–1.8."
"Axel Erikson was the first to patent -based FC technology in the year 1923... The characteristics, behaviour and structural applications of FC have been widely investigated..."
"FC, which is one of the varieties of cellular concrete[,] attracts... builders worldwide... has nice workability... can be used for thermal and sound isolation, flame protection as well as blast viscosity; nevertheless, low mechanical and physical characteristics... limit the scope of its application in concrete structures."